鋼板力學性能與化學成分
一般強度船體結構鋼力學性能與化學成份| 鋼材級別 |
屈服點 σs(MPa)不小于 |
抗拉強度 σb(MPa) |
伸長率σ% 不小于 |
碳 C |
錳 Mn |
硅 Si |
硫 S |
磷 P |
| A |
235 |
400-520 |
22 |
≤0.21 |
≥2.5 |
≤0.5 |
≤0.035 |
≤0.035 |
| B |
≤0.21 |
≥0.80 |
≤0.35 | |||||
| D |
≤0.21 |
≥0.60 |
≤0.35 | |||||
| E |
≤0.18 |
≥0.70 |
≤0.35 |
| 鋼材級別 |
屈服點σs (MPa)不小于 |
抗拉強度 σb(MPa) |
伸長率σ% 不小于 |
碳 C |
錳 Mn |
硅 Si |
硫 S |
磷 P |
| A32 |
315 |
440-570 |
22 |
≤0.18 |
≥0.9-1.60 |
≤0.50 |
≤0.035 |
≤0.035 |
| D32 | ||||||||
| E32 | ||||||||
| F32 |
≤0.16 |
≤0.025 |
≤0.025 | |||||
| A36 |
355 |
490-630 |
21 |
≤0.18 |
≤0.035 |
≤0.035 | ||
| D36 | ||||||||
| E36 | ||||||||
| F36 |
≤0.16 |
≤0.025 |
≤0.025 | |||||
| A40 |
390 |
510-660 |
20 |
≤0.18 |
≤0.035 |
≤0.035 | ||
| D40 | ||||||||
| E40 | ||||||||
| F40 |
≤0.16 |
≤0.025 |
≤0.025 |
| ||